ASTM A213 T11 Seamless boiler tube

ASTM A213 T11 is the part of ASTM A213 Standard Specification for Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, Heat-Exchanger Tubes.

These different requirements provide higher creep-rupture strength than normally achievable in similar grades without these different requirements. ASTM A213 T11 tubes shall be made by the seamless process and shall be either hot finished or cold finished, as specified. Grade TP347HFG shall be cold finished. Heat treatment shall be done separately and in addition to heating for hot forming. The ferritic alloy and ferritic stainless steels shall be reheated. On the other hand, austenitic stainless steel tubes shall be furnished in the heat-treated condition. Alternatively, immediately after hot forming, while the temperature of the tubes is not less than the minimum solution temperature, tubes may be individually quenched in water or rapidly cooled by other means. Tension test, hardness test, flattening test, and flaring test shall be done to each tube. Also, each tube shall be subjected to the nondestructive electric test or hydrostatic test.
ASTM A213 abstract is a brief summary of the referenced standard. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date.

Chemical Composition(%) for ASTM A213 T11 Low Alloy Steel

UNS Designation K11597
Carbon 0.05–0.15
Manganese 0.30–0.60
Phosphorus 0.025
Sulfur 0.025
Silicon 0.50–1.00
Nickel
Chromium 1.00–1.50
Molybdenum 0.44–0.65
Vanadium
Boron
Niobium
Nitrogen
Aluminum
Tungsten
Other Elements

Mechanical properties for ASTM A213 T11 Low Alloy Steel

Tensile strength(min) 415Mpa
Yield strength(min) 220Mpa
Elongation 30%
Delivery condition annealed

Ordering Information

Orders for material under this specification should include the following, as required, to describe the desired material adequately:

Quantity Feet, meters, or number of lengths
Name of material Seamless Alloy Steel Pipe
Grade STANDARD AND STEEL GRADE
Manufacture Hot-finished or cold-drawn
Size using one of the following:
NPS and Schedule Number
Outside Diameter and Nominal Wall Thickness
Length Specific or Random
End Finish

Packing:

Beveled/black painting/ plastic caps/ in bundles/ steel strips/ wooden protection

Inspection and Test:

Chemical Composition Inspection, Mechanical Properties Test(Tensile Strength, Yield Strength,Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test, Nodestructive Test, Hydrostatic Test.

Surface Treatment:

Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting, Epoxy & Fbe Coating Painting as requested.

ASTM A213 Standard Scope

1.1 This specification covers seamless ferritic and austenitic steel boiler, superheater, and heat-exchanger tubes, designated Grades T11, TP304, etc. These steels are listed in Tables 1 and 2.
1.2 Grades containing the letter, H, in their designation, have requirements different from those of similar grades not containing the letter, H. These different requirements provide higher creep-rupture strength than normally achievable in similar grades without these different requirements.
1.3 The tubing sizes and thicknesses usually furnished to this specification are 1/8 in. [3.2 mm] in inside diameter to 5 in. [127 mm] in outside diameter and 0.015 to 0.500 in. [0.4 to 12.7 mm], inclusive, in minimum wall thickness or, if specified in the order, average wall thickness. Tubing having other diameters may be furnished, provided such tubes comply with all other requirements of this specification.
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order.
TABLE 1 Chemical Composition Limits, %A, for Low Alloy SteelA Maximum, unless range or minimum is indicated. Where ellipses (…) appear in this table, there is no requirement, and analysis for the element need not be determined or reported.

B It is permissible to order T2 and T12 with a sulfur content of 0.045 max. See 16.3.

C Alternatively, in lieu of this ratio minimum, the material shall have a minimum hardness of 275 HV in the hardened condition, defined as after austenitizing and cooling to room temperature but prior to tempering. Hardness testing shall be performed at mid-thickness of the product. Hardness test frequency shall be two samples of product per heat treatment lot and the hardness testing results shall be reported on the material test report.

 

Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s